H. Huang, S. Y. Cheng, J. F. Gao, C. S. Chen and J. X. Yi (2014) Phase-inversion tape-casting preparation and significant performance enhancement of Ce0.9Gd0.1O1.95-La0.6Sr0.4Co0.2Fe0.8O3-delta dual-phase asymmetric membrane for oxygen separation. Journal/Materials Letters 137 245-248. [In English]
Web link: http://dx.doi.org/10.1016/j.matlet.2014.09.016
Keywords: Ceramic composites; Functional; Oxygen separation; Membrane; Phase; inversion; HOLLOW-FIBER MEMBRANE; PERMEATION; COMPOSITE; PERMEABILITY

Abstract: The dual-phase Ce0.9Gd0.1O1.95-La0.5Sr0.4Co0.2Fe0.8O3-delta asymmetric membrane was prepared via a phase-inversion tape-casting method. The membrane consisted of a thicker porous support layer and a thinner dense layer. When the dense side of the membrane was coated with a La0.5Sr0.4CoO3-delta catalytic activation layer, the oxygen permeation flux was markedly increased by a factor of 4.1-5.6, reaching 0.45 mL cm(-2) min(-1) at 900 degrees C. The flux increase can be attributed to enhanced surface oxygen exhange kinetics. (C) 2014 Elsevier B.V. All rights reserved.

 
 
相关链接
H. Huang, S. Y. Cheng, J. F. Gao, C. S. Chen and J. X. Yi (2014) Materials Letters 137 245-248.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号