K. Q. Zhou, Q. J. Zhang, J. J. Liu, B. Wang, S. H. Jiang, Y. Q. Shi, Y. Hu and Z. Gui (2014) Synergetic effect of ferrocene and MoS2 in polystyrene composites with enhanced thermal stability, flame retardant and smoke suppression properties. Journal/Rsc Advances 4 13205-13214. [In English]
Web link: http://dx.doi.org/10.1039/c3ra46334f
Keywords: POLY(VINYL ALCOHOL) NANOCOMPOSITES; LAYERED SILICATE NANOCOMPOSITES; DOUBLE HYDROXIDE NANOCOMPOSITES; FIRE SAFETY APPLICATIONS; LITHIUM-ION; BATTERIES; MOLYBDENUM-DISULFIDE; GRAPHITE OXIDE; GRAPHENE; PERFORMANCE; POLYMERS

Abstract: As a graphene-like layered nanomaterial, molybdenum disulfide (MoS2) has gained intensive attention from the materials community. In our research, MoS2 is firstly modified with ferrocene (Fe-MoS2) on a large scale and then is used as a nanofiller to prepare PS composites by a masterbatch-based melt blending method. The aim of our present study is to study the synergistic effect of ferrocene and MoS2 on the thermal stability, fire resistance and smoke suppression properties of the PS composites. It was found that the thermal stability of the PS composite was obviously enhanced upon the introduction of 3.0 wt% Fe-MoS2. The cone test results indicated that the PS/Fe-MoS2 composites exhibited superior flame retardance to PS/MoS2 and PS/ferrocene composites. Furthermore, the addition of Fe-MoS2 could improve the smoke suppression properties of PS composites, as evidenced by the reduction of the carbon monoxide production rate and smoke production rate (SPR). The total flammable gaseous products from the PS composites were decreased which further led to the inhibition of smoke. Such a significant improvement in thermal stability, fire resistance and smoke suppression properties was mainly attributed to good dispersion of the modified MoS2 nanosheets, synergistic effects between ferrocene and MoS2 nanosheets, physical barrier effects of MoS2 nanosheets and the presence of ferrocene and MoS2 can promote char formation simultaneously.

 
 
相关链接
K. Q. Zhou, Q. J. Zhang, J. J. Liu, B. Wang, S. H. Jiang, Y. Q. Shi, Y. Hu and Z. Gui (2014) Rsc Advances 4 13205-13214.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号