L. L. Jiao, H. H. Xiao, Q. S. Wang and J. H. Sun (2013) Thermal degradation characteristics of rigid polyurethane foam and the volatile products analysis with TG-FTIR-MS. Journal/Polymer Degradation And Stability 98 2687-2696. [In English]
Web link: http://dx.doi.org/10.1016/j.polymdegradstab.2013.09.032
Keywords: Rigid polyurethane foam, Thermal degradation, Volatile products, TG-DSC, In situ FTIR, TG-FTIR-MS, PENTANE, DECOMPOSITION, BEHAVIOR
Abstract: Thermal degradation characteristics of rigid polyurethane (PUR) foam in both air and nitrogen gaseous environments were studied using thermogravimetry and differential scanning calorimetry (TG-DSC) hyphenated techniques. And in situ Fourier Transform Infrared (FTIR) was employed to investigate the characteristic functional groups of the decomposition residues at different temperatures. It is found that the thermal degradation of FUR material in air and N-2 present a three-stage and a two-stage process, respectively. And the degradation reaction rate of FUR in air is accelerated significantly due to the presence of oxygen. The thermal degradation mechanism of FUR under non-oxidizing gaseous environment was evaluated using a TGA instrument coupled with Fourier Transform Infrared and mass spectrometer (TG-FTIR-MS). HCFC-141b served as blowing agent is detected at the initial stage. The urethane bond groups of FUR start to break up into isocyanates segments and polyols segments from about 200 degrees C. With an increase of temperature, the polyols decompose into some kinds of aliphatic ether alcohol. In the temperature range of 350-500 degrees C, the dominant volatile products are primary amines, secondary amines, vinyl ethers and CO2. (C) 2013 Elsevier Ltd. All rights reserved.