Wang ZZ, Shen XF, Fan WC, Hu Y, Qu BJ, Gui Z (2002) Polymer International 51(7), 653-657.
文章来源:WOS    作者:SKLFS    发布时间:2011-08-16

Wang ZZ, Shen XF, Fan WC, Hu Y, Qu BJ, Gui Z (2002) Effects of poly(ethylene-co-propylene) elastomer on mechanical properties and combustion behaviour of flame retarded polyethylene/magnesium hydroxide composites. Polymer International 51(7), 653-657. [In English]

Web link: http://dx.doi.org/10.1002/pi.941

Keywords:

polyethylene; magnesium hydroxide; mechanical properties; combustion; characteristics; poly(ethylene-co-propylene); elastomer; crystallization; magnesium-hydroxide; polypropylene composites; tensile properties; crystallization; blends; filler

Abstract: Magnesium hydroxide-based halogen-free flame retarded linear low density polyethylene composites containing poly(ethylene-co-propylene) elastomer were prepared in the melt process and subsequently vulcanized thermally. Influences of the elastomer on the mechanical properties, combustion characteristics and crystallization behaviour of polyethylene/magnesium hydroxide composites have been investigated. The results from the mechanical tests show that the incorporation of a suitable amount of elastomer into polyethylene/magnesium hydroxide composites after vulcanization can increase both the tensile strength and elongation greatly, compared with those of the composites without the elastomer. It has been found that the properties such as limiting oxygen index, UL-94 rating, the time to ignition and the rate of heat release of polyethylene/magnesium hydroxide/elastomer composites are all improved in comparison with polyethylene/magnesium hydroxide composites at the same retardant level. Scanning electron microscopy studies show that the incorporation of the elastomer into polyethylene/magnesium hydroxide composites improves the compatibility between the filler and the polymer substrate. The degrees of crystallinity of polyethylene/magnesium hydroxide/elastomer composites decrease with increasing the elastomer content. (C) 2002 Society of Chemical Industry.

 
 
相关链接
Wang ZZ, Shen XF, Fan WC, Hu Y, Qu BJ, Gui Z (2002) Polymer International 51(7), 653-657.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号