Cai YB, Hu Y, Xiao JF, Song L, Fan WC, Deng HX, Gong XL, Chen ZY (2007c) Morphology, thermal and mechanical properties of poly (styrene-acrylonitrile) (SAN)/clay nanocomposites from organic-modified montmorillonite. Polymer-Plastics Technology and Engineering 46(5), 541-548. [In English]

Web link: http://dx.doi.org/10.1080/03602550701298655

Keywords:

montmorillonite(MMT); nanocomposites; OMT-CPC; OMT-P16; organic-modified; montmorillonite (OMT); poly (styrene-acrylonitrile) (SAN); layered-silicate nanocomposites; oligomerically-modified clay; emulsion; polymerization; fire properties; intercalation; copolymer; hybrid; polypropylene; flammability

Abstract: Poly (styrene-acrylonitrile) (SAN)/clay nanocomposites have successfully been prepared by melt intercalation method. The hexadecyl triphenyl phosphonium bromide (P16) and cetyl pyridium chloride (CPC) are used to modify the montmorillonite (MMT). The structure and thermal stability property of the organic modified MMT are, respectively characterized by Fourier transfer infrared (FT-IR) spectra, X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The results indicate that the cationic surfactants intercalate into the gallery of MMT and the organic-modified MMT by P16 and CPC has higher thermal stability than hexadecyl trimethyl ammonium bromide (C16) modified MMT. The influences of the different organic modified MMT on the structure and properties of the SAN/clay nanocomposites are investigated by XRD, transmission electronic microscopy (TEM), high-resolution electron microscopy (HREM), TGA and dynamic mechanical analysis (DMA), respectively. The results indicate that the SAN cannot intercalate into the interlayers of the pristine MMT and results in microcomposites. However, the dispersion of the organic-modified MMT in the SAN is rather facile and the SAN nanocomposites reveal an intermediate morphology, an intercalated structure with some exfoliation and the presence of small tactoids. The thermal stability and the char residue at 700 degrees C of the SAN/clay nanocomposites have remarkably enhancements compared with pure SAN. DMA measurements show that the silicate clays improve the storage modulus and glass transition temperature (Tg) of the SAN matrix in the nanocomposites.

 
 
相关链接
Cai YB, Hu Y, Xiao JF, Song L, Fan WC, Deng HX, Gong XL, Chen ZY (2007c) Polymer-Plastics Technology and Engineering 46(5), 541-548.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号