Zhan J, Song L, Nie SB, Hu YA (2009b) Polymer Degradation and Stability 94(3), 291-296.
文章来源:WOS    作者:SKLFS    发布时间:2011-08-16

Zhan J, Song L, Nie SB, Hu YA (2009b) Combustion properties and thermal degradation behavior of polylactide with an effective intumescent flame retardant. Polymer Degradation and Stability 94(3), 291-296. [In English]

Web link: http://dx.doi.org/10.1016/j.polymdegradstab.2008.12.015

Keywords:

Polylactide; Intumescent flame retardant; Combustion property; Thermal; stability; renewable resources; lactic-acid; fire; mechanism; polymers

Abstract: An intumescent flame retardant spirocyclic pentaerythritol bisphosphorate disphosphoryl melamine (SPDPM) has been synthesized and its structure was characterized by Fourier transformed infrared spectrometry (FTIR), (1)H and (31)P nuclear magnetic resonances (NMR). A series of polylactide (PLA)-based flame retardant composites containing SPDPM were prepared by melt blending method. The combustion properties of PLA/SPDPM composites were evaluated through UL-94, limiting oxygen index (LOI) tests and microscale combustion calorimetry (MCC) experiments. It is found that SPDPM integrating acid, char and gas sources significantly improved the flame retardancy and anti-dripping performance of PLA. When 25 wt% flame retardant was added, the composites achieved UL-94 V0, and the LOI value was increased to 38. Thermogravimetric analysis (TGA) showed that the weight loss rate of PLA was decreased by introduction of SPDPM. In addition, the thermal degradation process and possible flame retardant mechanism of PLA composites with SPDPM were analyzed by in situ FTIR. (C) 2008 Elsevier Ltd. All rights reserved.

 
 
相关链接
Zhan J, Song L, Nie SB, Hu YA (2009b) Polymer Degradation and Stability 94(3), 291-296.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号