Xu WZ, Lu B, Hu Y, Yin JG, Zhang YY (2011) Asian Journal of Chemistry 23(5), 2284-2288.
文章来源:WOS    作者:SKLFS    发布时间:2011-08-16

Xu WZ, Lu B, Hu Y, Yin JG, Zhang YY (2011) Synthesis and Characterization of Novel Fluorinated Polyurethane Elastomers. Asian Journal of Chemistry 23(5), 2284-2288. [In English]

Web link:

Keywords:

Fluorinated diamine; Fluorinated polyurethane elastomer; Surface; property; Flame retardancy; chain extenders; segmented polyurethanes; phosphine oxide; polyimides

Abstract: A series of fluorinated polyurethane elastomers were synthesized from 2-trifluoromethyl-4,4'-diaminodiphenyl ether, which was derived from 2-chlorobenzotrifluoride and p-nitrophenol. The structure and properties of fluorinated polyurethane elastomers were measured by fourier transform infrared spectroscopy, thermogravimetric analysis, microscale combustion colorimeter, water absorption and contact angle measurement. The results show the fluorinated polyurethane elastomers prepared from 2-trifluoromethyl-4,4'-diammodiphenyl ether have lower surface tension, better hydrophobic property and thermal stability and good mechanical properties. Furthermore, the introduction of fluorine into fluorinated polyurethane elastomers improved the flame retardancy. With the content of fluorine increasing from 1.5 to 2.8%. the peak heat release rate and total heat release decreased from 605.4 w/g and 23.7 kJ/g to 511.0 w/g and 22.4 kJ/g, indicating that the flame retardant property of polyurethane elastomer increased with the increase in the fluorine content.

 
 
相关链接
Xu WZ, Lu B, Hu Y, Yin JG, Zhang YY (2011) Asian Journal of Chemistry 23(5), 2284-2288.
联系我们
安徽省合肥市金寨路96号
中国科学技术大学
火灾安全全国重点实验室
邮政编码:230026
   
Tel:(+86)551 63601651
Fax:(+86)551 63601669
E-mail:sklfs@ustc.edu.cn
Copyright © 1990-2011 State Key Laboratory of Fire Science, University of Science and Technology of China
火灾科学国家重点实验室 版权所有 皖ICP备:002106505 号